파절저항성
제품명 | K1C*(mm^1/2MPa) | Std. Dev.(mm^1/2MPa) |
Belleglass Op. Dent. D.C. | 1.48 | 0.09 |
Herculite XRV | 1.00 | 0.05 |
Cristobal + | 1.14 | 0.27 |
Sinfony | 1.12 | 0.05 |
Artglass Dentin | 1.17 | 0.05 |
Targis | 0.89 | 0.12 |
Dentin (1) | 3.08 | 0.33 |
Enamel (2) | 0.7-1.27 |
* ASTM E399-81 (Single-Edge Notched-Bend, a/W=1/2)
(1) O.M. El Mowafy, D.C. Watts; J. Dent. Res. 65(5):677-681, May, 1986.
(2) Hassan, R. et al, J. Dent. Res. 60:820-827, 1981
굴절강도(F.S.)와 탄성계수 (E)
제품명 | F.S., MPa (s.d.) | E, GPa (s.d.) |
Belleglass Op. Dent. D.C. | 158 (11) | 21.0 (14.0) |
Herculite XRV | 142 (10) | 13.1 (0.7) |
Cristobal + | 179 (11) | 13.0 (0.4) |
Sinfony | 89 (8) | 3.6 (0.3) |
Artglass Dentin | 109 (10) | 8.3 (0.4) |
Targis | 142 (23) | 10.3 (0.6) |
Dentin(1,2) | 52 | 18 |
Enamel (1) | 10 | ---- |
(1) Albers, H. Adept Report, p.1-20, 6(2),Spring, 1999
(2) O.M. El Mowafy, D.C. Watts; J. Dent. Res. 65(5):677-681,
May, 1986.
부피수축/체적의 정확도
제품명 | Vol. % 수축률* (Vol.%) | Std. Dev. |
Belleglass Op. Dent. D.C. | 0.9 | 0.1 |
Herculite XRV | 2.9 | 0.2 |
Cristobal + | 3.3 | 0.3 |
Sinfony | 4.5 | 0.1 |
Artglass Dentin | 3.3 | 0.2 |
Targis | 3.0 | 0.1 |
* buoyancy법에 의한 부피중합수축률
온도관련 요소
제품명 | CTE(ppm/C) | Std. Dev.(ppm/C) |
Belleglass Op. Dent. D.C. | 13.1 | 0.7 |
Herculite XRV | 30.3 | 0.8 |
Cristobal + | 27.0 | 1.0 |
Sinfony | 62.6 | 3.0 |
Artglass Dentin | 33.3 | 1.2 |
Targis | 28.2 | 0.6 |
Dentin (1) | 11.4 | |
Enamel (2) | 12 |
(1) Skinner and Phillips: The Science of Dental Materials W.B. Saunders, 1967.
(2) ADA: Guide to Dental Materials and Devices, ADA, Chicago, 1974.
목적: 본 연구의 목적은 5종의 간접콤포지트 레진을 6종의 알로이에 결합시켜 24시간후 열처리후의 결합강도를 측정하기 위한 것임.
결과: 열처리한 24시간후의 평균결합강도 (MPa)
Alloy | AG | BG | SC | SI | TG |
HG | 9.6 | 27.8 | 16.1 | 19.4 | 10.5 |
LG | 20.6 | 29.1 | 27.2 | 29.2 | 17.6 |
CC | 19.6 | 26.3 | 15.8 | 24.4 | 29.4 |
NC | 25.9 | 36.4 | 15.0 | 27.3 | 36.8 |
P | 18.6 | 17.0 | 20.3 | 16.7 | 14.0 |
T | 21.5 | 25.0 | 18.6 | 25.3 | 24.6 |
AG=Artglass, BG=Belleglass, SC=Sculpture, SI=Sinfony, TG= Targis
HG= high gold, LG= low gold, CC= chrome cobalt, NC= nickel chromium,P= palladium, T= titanium.
결론: …열처리후, BG는 다른 제품에 비해 상당히 높은 수치를 나타냄.
내부결합사진-샌드블라스팅 및 HF 에칭된 표면
Premise Indirect 시스템Premise Indirect 재료Premise Indirect 인레이 & 온레이축성시 순측 상아질쪽의 두께는 최대 1.5mm를 넘지 않아야 한다.